TMT Bars

Home  /  TMT Bars

TMT Bars

Manufacturing Process

Ashok Steel TMT Bars are manufactured from superior quality billets, in adherence with the international quality standards and norms to ensure quality consistency. All billets are casted from first class ore sourced from high grade ore with exceptional chemical composition. The billets go through a test process to maintain the certified composition of Carbon, Sulphur and Phosphorus in the Rebar sections which makes them the best choice for construction.These are essential for being in compliance with tolerance parameters and high dimensional accuracy.

TMT Bar Features

Sturdy Build Ashok Steel TMT Bars exhibit consistent superior strength and high ductility which ensures superior structures. Corrosion Resistant The controlled thermo mechanical treatment results in an uniform and thick tempered martensitic rim, completely free from internal stress. This martensitic rim improves the corrosion resistance as well as fatigue strength. Seismic Resistance They support Seismic design due to its unique combination of strength, ductility and stress ratio.

Mechanical Properties

The advanced manufacturing process of Ashok Steel TMT Bars makes it well surpass the minimum limit of strength and ductility specified in the standard IS: 1786. The yield strength also far exceeds the standard norms and specifications. The UTS/YS ratio and percentage elongation that determine the seismic property of a rebar, is also very high in Ashok Steel TMT Bars. This significantly enhance its ability to handle the pressure of earthquakes.

Product Range

Section

(mm)

Nominal weight

(kg/meter)

Tolerance
5.6 0.194 +-7%
8 0.395 +7%
10 0.617 +7%

Earthquake Resistance

The tests are conducted on concrete beam column joints with repeated reverse loading and large deformation, a real life earthquake scenario alike. Uniform energy dissipation for each cycle indicates high ductility and superior seismic resistant properties for Ashok Steel TMT Bars. This is essential for minimizing structural damages and human casualties

BIS Specifications for Chemicals Property
 Chemicals Property(Maximum) Fe 500 Fe 500-D

TopTech 500 D

(Typical Maximum Value)

%Carbon 0.300 0.250 0.250
%Corbon Equivalent(CE) 0.420 0.420 0.400
%Sulfur(S) 0.055 0.040 0.035
%Phosphorus(P) 0.055 0.040 0.035
%Sulfur & Phosphorus(S&P) 0.105 0.075 0.070
%Nitrogen(PPM) 120 120 120
BIS Specifications for Mechanical Propertries
 Mechanical Propertries (Maximum) Fe 500 Fe 500-D

TopTech 500 D

(Typical Maximum Values)

Yield Stess-YS(N/mm2) 500 500 520
UItimate TensileStress-UTS(N/mm2) 545 565 620
UTS/YS Ratio 1.08 110 115
Top